    模拟古代灰口铸铁的三种表面状态在碱液中的电化学行为
    The Electrochemical Behavior of Three Kinds of Surface State Simulation of Ancient Grey Cast Iron in Lye

  • 全文下载: PDF(988KB) HTML   XML   PP.41-47   DOI: 10.12677/AMC.2016.43005  
  • 下载量: 181  浏览量: 741  

作者:  

赵东明,何积铨:北京科技大学新材料技术研究院,北京

关键词:
模拟古代灰口铸铁表面状态电化学行为Simulated Ancient Iron Relics Surface State Electrochemical Behavior

摘要:

采用极化曲线法,研究模拟古代灰口铸铁的裸表面、无氯有锈表面和除氯后表面三种表面在碱液中的电化学行为,结果表明,模拟古代灰口铸铁在亚硝酸钠溶液环境中,存在特定的[ ]/[ ]比值,可以使得亚硝酸钠对钝化膜的修复作用与氯离子对钝化膜的破坏作用达到动态平衡,这个动态平衡点为估算除氯后锈层中含氯量(即除氯程度)提供可能性。

By using polarization curve methods, this paper studied the electrochemical behaviors of three surfaces in lye including the bare surface of simulated ancient grey cast iron, rust surface and sur-face after chloride removal. The result showed that simulated ancient grey cast iron under NaNO2 environments had certain [ ]/[ ] quality ratio. A dynamic balance was achieved between repairing effect to passive film by NaNO2 and damage effect to passive film by chloride ion. This dynamic point may help to estimate the chloride chlorinity in the rust layer which also called the dechlorination level.

文章引用:
赵东明, 何积铨. 模拟古代灰口铸铁的三种表面状态在碱液中的电化学行为[J]. 材料化学前沿, 2016, 4(3): 41-47. http://dx.doi.org/10.12677/AMC.2016.43005

参考文献

[1] 吴天才. 出土铁器文物的脱盐[J]. 考古与文物, 2003(4): 94-96.
[2] 国家文物局博物馆与社会文物司, 编. 博物馆铁质文物保护技术手册[M]. 北京: 文物出版社, 2011.
[3] 范庆新, 邓春林, 韦江雄. 混凝土中钢筋锈蚀的电化学无损检测技术[J]. 武汉理工大学学报, 2008, 30(3): 70-73.
[4] 夏春兰. 铁极化曲线的测定及应用实验研究[J]. 大学化学, 2003, 18(5): 38-41.
[5] 罗刚, 施养抗. 钢筋混凝土构件中钢筋锈蚀量的无损检测方法[J]. 福建建筑, 2002(4): 55-57.
[6] 尚素红. 电化学脉冲除氯技术应用基础研究[D]: [硕士学位论文]. 北京: 北京科技大学, 2014.
[7] 杜荣归, 刘玉, 林昌健. 氯离子对钢筋腐蚀机理的影响及其研究进展[J]. 材料保护, 2006(6): 45-50.
[8] 乔冰. 氯离子对钢筋腐蚀行为的影响及其缓蚀剂的研究[D]: [硕士学位论文], 厦门: 厦门大学, 2009.
[9] 程霞, 何积铨, 朱自勇. 电化学方法在砂浆样除氯方面的应用研究[J]. 化工技术与开发, 2012(1): 4-7.