整体式铜钴复合氧化物催化剂的乙酸乙酯催化燃烧性能
Catalytic Combustion Performance of Ethyl Acetate with Copper-Cobalt Composite Oxide Catalysts
摘要:
以堇青石蜂窝陶瓷为载体,采用涂覆法制备了一系列不同摩尔比的Cu-Co复合氧化物催化剂并测试了催化剂的乙酸乙酯催化燃烧性能。当Cu与Co摩尔比为1:2时,该催化剂(1Cu2Co)具有较高的乙酸乙酯催化活性(T99 = 250℃)。运用X射线衍射(XRD),程序升温还原(H2-TPR),物理吸附(BET)等技术对催化剂进行了表征。结果表明,较高的比表面积(170 m2/g),较小的CuO和CoOx晶粒以及较强的还原性能为1Cu2Co催化剂高活性的主要原因。
Abstract: A series of Cu-Co catalysts with different Cu-Co mass ratios were prepared via coating method with the cordierite honeycomb ceramic as the carrier, and the catalytic combustion performance of ethyl acetate is tested. The highest activity (T99 = 250˚C) occurred at mole ratio of 1:2 for Cu:Co (1Cu2Co). The catalysts were further characterized by X-ray diffraction (XRD), Brunauer-Emmett- Teller (BET), and temperature-programmed reduction (H2-TPR) technologies. The results showed that the main reasons of higher activity of 1Cu2Co catalysts can be attributed to the enhanced reducibility, higher surface area (170 m2/g), and smaller crystal size of CuO and CoOx。
参考文献
[1]
|
李国文 (1998) 挥发性有机废气(VOCs)的污染控制技术. 西安建筑科技大学学报, 4, 399-402.
|
[2]
|
Spivey, J.J. (1987) Complete catalytic oxidation of volatile organics. Industrial Engineering Chemistry Research, 26, 2165-2171.
|
[3]
|
Urashima, K. and Chang, J.S. (2000) Removal of volatile organic compounds from air streams and industrial flue gases by non-thermal plasma technology. IEEE Transactions on Industry Applications, 7, 602-614.
|
[4]
|
朱乐天 (2002) 室内空气污染控制. 化学工业出版社, 北京.
|
[5]
|
Koichi, E. and Hiromichi, A. (2001) Low tem-perature oxidation of methane over Pd-based Catalysts-effect of support oxide on the combustion activity. Applied Ca-talysis, 359-367.
|
[6]
|
郭建光, 李忠, 奚红霞, 等 (2004) 催化燃烧VOCs的三种过渡金属催化剂的活性比较. 华南理工大学学报(自然科学版), 5, 56-59.
|
[7]
|
黄海凤, 唐伟 (2004) Cu-Mn复合氧化物及稀土助剂对VOCs催化燃烧性能的研究. 浙江工业大学学报, 4, 407-411.
|
[8]
|
Marion, M.C., Garbowski, E. and Primet, M. (1991) Catalytic properties of copper oxide supported on zinc aluminate in methane combustion. Journal of the Chemical Society, Faraday Transactions, 87, 1795-1800.
|
[9]
|
Radwan, N.R.E., Mokhtar, M. and El-Shobaky, G.A. (2003) Surface and catalytic properties of CuO and Co3O4 solids as influenced by treatment with Co2+ and Cu2+ species. Applied Catalysis A, 241, 77.
|
[10]
|
Tien-Thao, N., Zahedi-Niaki, M.H., Alamdari, H. and Kaliaguine, S. (2007) Effect of alkali additives over nanocrystalline Co-Cu-based perovskites as catalysts for higher-alcohol synthesis Journal of Catalysis, 245, 348.
|