标题:
42CrMo调质钢碳氮共渗组织及性能研究Study of Microstructure and Properties on Quenched and Tempered 42CrMo Steel after Carbonitriding
作者:
王乐, 王晓溪, 徐昊, 刘壮, 张飞飞, 陈方旭
关键字:
42CrMo调质钢, 碳氮共渗, 组织性能Quenched and Tempered 42CrMo Steel, Carbonitriding, Microstructure and Properties
期刊名称:
《Metallurgical Engineering》, Vol.2 No.2, 2015-06-05
摘要:
采用碳氮共渗工艺,对42CrMo调质钢进行表面强化处理,研究了其组织变化对力学性能的影响。结果表明,经碳氮共渗工艺后,工件表面产生了一层0.14 mm厚的碳氮化合物层,芯部转变为隐晶马氏体加铁素体,材料组织得到了进一步细化,42CrMo调质钢的表面硬度达到650 HV,屈服强度达到1120 MPa,冲击韧性达到84 J/cm2。实验结果表明,销轴经碳氮共渗热处理后,42CrMo调质钢具有更好的强韧性,产品质量提高。Using carbonitriding process, the processing of quenched and tempered 42CrMo steel surface was strengthened, and the effect of its microstructure change on mechanical properties was investi-gated. The results show that, after carbonitriding process, a carbonitride layer of 0.14 mm is pro-duced on the workpiece surface; core is transformed into cryptocrystalline martensite and ferrite; material organization has been further refined; the surface hardness of quenched and tempered 42CrMo steel is 650 HV; the yield strength is 1120 MPa; and the impact toughness can reach 84 J/cm2. The experimental results show that after carbonitriding heat treatment of the pin, quenched and tempered 42CrMo steel has better tenacity, and the product quality is improved.