溶剂热法制备LaF3:Ce3+/Tb3+晶体及功能化Synthesis of LaF3:Ce3+/Tb3+ Crystals via Solvothermal Method and Functionalization
作者:
张艺
关键字:
溶剂热法, 聚丙烯酸(PAA), 功能化材料, LaF3Solvothermal Method, Poly(acrylic acid) (PAA), Functionalized Materials, LaF3
期刊名称:
《Studies in Synthetic Chemistry》, Vol.3 No.2, 2015-08-10
摘要:
采用溶剂热法,乙醇和乙二醇为混合溶剂,160℃条件下,反应12小时,成功制备了LaF3:Ce3+/Tb3+晶体。并用聚丙烯酸(PAA)对材料进行了功能化,红外吸收光谱显示材料表面成功修饰上羧基(-COOH)。以275 nm为激发波长,LaF3:Ce3+/Tb3+及COOH-LaF3:Ce3+/Tb3+晶体的发射波长均为526 nm,而功能化的LaF3:Ce3+/Tb3+荧光强度较低。
The LaF3:Ce3+/Tb3+ crystals were prepared using solvothermal method, at 160˚C for 12 h in the mixed solvents of ethanol and glycol. The as-prepared LaF3:Ce3+/Tb3+ crystals were functionlized with Poly(acrylic acid). IR absorption spectra showed that the carboxyl group (-COOH) is on the surface of LaF3:Ce3+/Tb3+ crystals. Under 275 nm excitation, the emission peaks of LaF3:Ce3+/Tb3+ and COOH-LaF3:Ce3+/Tb3+ crystals locate at 526 nm. Moreover, the fluorescent intensity of the functional LaF3:Ce3+/Tb3+ is lower.