    手机背板用氧化锆陶瓷流延片烧结工艺研究
    Research on the Sintering Process of the Zirconia Ceramics Tape Casting Uropatagia as the Backboard of the Mobile Phone

  • 全文下载: PDF(983KB) HTML   XML   PP.442-448   DOI: 10.12677/MS.2016.66055  
  • 下载量: 1,370  浏览量: 3,683  

作者:  

黄咸波,谢光远,赵 芃,巩 俐,林寒月,杜 聪:武汉科技大学青山校区,湖北 武汉

关键词:
氧化锆陶瓷手机背板装炉方式整平处理Zirconia Ceramics Backboard of the Mobile Phone Placing Mode Smoothing Process

摘要:

本文比较分析了作为手机背板的氧化锆流延基片烧结过程中的变形与自由平放、压重、腾空三种装炉方式之间的关系,探究了用于平复氧化锆手机背板翘曲的整平处理工艺。结果表明压重装炉方式和腾空装炉方式可用于限制在作为手机背板的氧化锆流延基片烧结过程中的变形,其中压重装炉方式不适合大面积薄片流延基片的烧结;采用腾空装炉方式烧结的氧化锆流延基片,经过在1400℃保温4小时的整平处理,可以得到较为平整的手机背板。

This paper compares and analyzes the relationship between the deformation of the zirconia tape casting uropatagia used as the mobile phone backboard during the sintering process and three placing modes including free placement, ballasting placement and placing baffle a certain height fromuropatagia, and it also researches the smoothing process used for smooth the warping zirconia backboard of the mobile phone. The result showed that ballasting placement and placing baffle a certain height from uropatagia can be used to restrain the deformation of the zirconia tape casting uropatagia used as the mobile phone backboard during the sintering process. Among it, ballasting placement was not suitable for the sintering of large-area tape casting uropatagia; and the zirconia tape casting uropatagia sintered by means of placing baffle a certain height from uropatagia could be made into relatively smooth mobile phone backboard after the smoothing process, maintaining sintering temperature at 1400˚C for four hours.

文章引用:
黄咸波, 谢光远, 赵芃, 巩俐, 林寒月, 杜聪. 手机背板用氧化锆陶瓷流延片烧结工艺研究[J]. 材料科学, 2016, 6(6): 442-448. http://dx.doi.org/10.12677/MS.2016.66055

参考文献

[1] 熊炳坤, 林振汉, 等. 二氧化锆制备工艺与应用[M]. 北京: 冶金工业出版社, 2008: 1-3.
[2] 任永国, 刘自强. 氧化锆材料种类及应用[J]. 中国陶瓷, 2008, 4(4): 44-45.
[3] 张玉军, 张伟儒, 等. 结构陶瓷材料及其应用[M]. 北京: 化学工业出版社, 2005: 9-13.
[4] 李冬云, 乔冠军, 金志浩. 流延法制备陶瓷薄片的研究进展[J]. 硅酸盐学报, 2004(2): 44-47.
[5] 程锦然, 编译. 电泳法成型超薄陶瓷基片[J]. 佛山陶瓷, 2004(4): 40-42.
[6] Li, W. and Gao, L. (2000) Rapid Sintering of Nanocrystalline ZrO2(3Y) by Spark Plasma Sintering. Journal of the European Ceramic Society, 20, 2441-2445. https://doi.org/10.1016/S0955-2219(00)00152-7
[7] 刘晓光, 李斌太, 李国军, 陈大明, 李爱兰. 水基凝胶注模法制备稳定氧化锆胚体的研究[J]. 硅酸盐通报, 2003(6): 68-71.
[8] 胡志军, 曹峰, 桂文涛. 凝胶浇注制备高性能氧化锆陶瓷的研究[J]. 武汉理工大学学报, 2006, 28(1): 13-15.
[9] 南充三环电子有限公司, 潮州三环(集团)股份有限公司. 一种氧化锆陶瓷手机后盖的制备方法[P]. 中国专利, 2015103092851. 2015-06-08.
[10] 刘忠军, 奚正平, 汤慧萍, 汪强兵, 王培. 烧结应力研究进展[J]. 稀有金属材料与工程, 2010, 39(9): 1687-1688.