    喷雾干燥法制备LiNi0.5Co0.2Mn0.3O2正极材料及其性能研究
    Synthesis of LiNi0.5Co0.2Mn0.3O2 Cathode Material by Spray-Drying Method and Its Electrochemical Performance

  • 全文下载: PDF(840KB) HTML   XML   PP.72-77   DOI: 10.12677/MS.2017.71010  
  • 下载量: 833  浏览量: 1,086  

作者:  

谢罗生:广西自治区质量技术监督局,广西 南宁;
林乔青,李华成,王春飞,胡明超,黄瑞鸿:中信大锰矿业有限责任公司,广西 南宁;
王正国:苏州大学,江苏 苏州

关键词:
锂离子电池正极材料LiNi0.5Co0.2Mn0.3O2喷雾干燥Lithium Ion Batteries Cathode Materials LiNi0.5Co0.2Mn0.3O2 Spray-Drying

摘要:

采用喷雾干燥法合成了LiNi0.5Co0.2Mn0.3O2正极材料。XRD表明样品均为纯相,无其它杂相存在。SEM研究表明,各样品均为类球形结构,温度升高颗粒粒径增大。电化学研究表明,900℃下合成的样品具有最优的电化学性能,该样品在0.1C倍率下的首次放电比容量为163.0 mAh∙g−1,循环50次后的容量保持率为92.6%。

LiNi0.5Co0.2Mn0.3O2 cathode materials were synthesized by the spray-drying method. XRD results reveal that the samples are pure phase and no impurities are detected. SEM results indicate that the samples show similar spherical particles. The particle size increases with the synthesis tem-perature. Electrochemical tests show that the sample synthesized at 900˚C exhibits the best elec-trochemical performance. The sample shows the initial discharge specific capacity of 163.0 mAh∙g−1 at 0.1C rate and possesses the capacity retention of 92.6% after 50 cycles.

文章引用:
谢罗生, 林乔青, 李华成, 王正国, 王春飞, 胡明超, 黄瑞鸿. 喷雾干燥法制备LiNi0.5Co0.2Mn0.3O2正极材料及其性能研究[J]. 材料科学, 2017, 7(1): 72-77. http://dx.doi.org/10.12677/MS.2017.71010

参考文献

[1] Li, L., Chen, Z., Song, L., et al. (2015) Characterization and Electrochemical Performance of Lithium-Active Titanium Dioxide Inlaid LiNi0.5Co0.2Mn0.3O2 Material Prepared by Lithium Residue-Assisted Method. Journal of Alloys and Compounds, 638, 77-82. https://doi.org/10.1016/j.jallcom.2015.03.071
[2] Hou, P., Wang, X., Song, D., et al. (2014) Design, Synthesis, and Performances of Double-Shelled LiNi0.5Co0.2Mn0.3O2 as Cathode for Long-Life and Safe Li-Ion Battery. Journal of Power Sources, 265, 174-181. https://doi.org/10.1016/j.jpowsour.2014.04.107
[3] 张睿, 吴元欣, 何云蔚, 等. Li3PO4掺杂的Li(Ni0.5Co0.2Mn0.3)O2锂离子电池正极材料的流变相法合成及电化学性能表征[J]. 化工学报, 2015(8): 3177-3182.
[4] Qu, X.L., Zhang, Z.F., Cheng, J., et al. (2015) Study on Preparation of LiNi0.5Co0.2Mn0.3O2 Precursor-Spherical Ni0.5Co0.2Mn0.3O2(OH)2 [J]. Materials Science Forum, 816, 676-681.
[5] 邢军龙, 王启岁, 杨续来. 粒径对锂离子电池正极材料性能的影响[J]. 电源技术, 2015(39): 1852-1854.
[6] 赵瑞顼, 杨子莲, 杜鹏, 等. 锂源对固相合成LiNi0.5Co0.2Mn0.3O2正极材料性能的影响[J]. 华南师范大学学报(自然科学版), 2015(2): 48-52.
[7] 马全新, 孟军霞, 杨磊, 曹文. 锂离子电池正极材料LiNi0.5Co0.2Mn0.3O2的制备及电化学性能[J]. 中国有色金属学报, 2013, 23(2): 456-462.
[8] Aurbach, D., Srur-Lavia, S., Ghanty, C., et al. (2015) Studies of Aluminum-Doped LiNi0.5Co0.2Mn0.3O2: Electrochemical Behavior, Aging, Structural Transformations, and Thermal Characteristics. Journal of the Electrochemical Society, 162, A1014-A1027. https://doi.org/10.1149/2.0681506jes