    硫酸钠对钠化焙烧过程中钒渣浸出行为的影响
    Effect of Sodium Sulfate on the Phase Transformation and Leaching Behavior of Vanadium Slag in the Roasting Process

  • 全文下载: PDF(2570KB) HTML   XML   PP.91-96   DOI: 10.12677/MEng.2017.42013  
  • 下载量: 532  浏览量: 1,000  

作者:  

刘保瑶,史培阳,姜茂发:东北大学冶金学院,多金属共生矿生态化冶金教育部重点实验室,辽宁 沈阳

关键词:
钒渣钠化焙烧浸出硫酸钠Vanadium Slag Sodium Roasting Leaching Sodium Sulfate

摘要:

合理的钒渣钠化焙烧工艺对钒的提取至关重要,直接关系到钒产品质量和生产成本。本文针对不同钒渣复合钠化焙烧工艺进行研究,探讨相转变行为对钒渣浸出机制的影响作用,结果表明:钒渣采用单一碳酸钠焙烧工艺与复合焙烧工艺进行对比,复合焙烧工艺的钒相转化率和收率略有提高,随着硫酸钠配入量的增加,硅和磷元素浸出率略有降低。随着焙烧时间的延长,钒、硅和磷元素的浸出率呈逐渐增大的趋势;在860℃条件下,采用复合钠化焙烧,Na2SO4配入量应控制在3%~9%,时间在30~60 min较为适宜。

Reasonable process of vanadium slag roasting is very important to the extraction of vanadium, which is directly related to the quality and the cost of the products. In order to investigate the effect of phase transition behavior on the leaching mechanism of vanadium slag, different complex sodium roasting processes of vanadium slag were discussed. Results are shown as follows. Com-pared with in single sodium roasting process, the phase transformation efficiency and yield in complex sodium roasting process are slightly higher. With increase in the proportion of the sodium sulfate quantity, the leaching efficiencies of silicon and phosphorus decrease slightly. With the extension of roasting time, the leaching efficiencies of vanadium, silicon and phosphorus gradually increase. Adopting complex sodium roasting process at 860˚C, the proportion of the Na2SO4 quantity should be controlled at 3%~9%, and the time is suitable between 30 to 60min.

文章引用:
刘保瑶, 史培阳, 姜茂发. 硫酸钠对钠化焙烧过程中钒渣浸出行为的影响[J]. 冶金工程, 2017, 4(2): 91-96. https://doi.org/10.12677/MEng.2017.42013

参考文献

[1] 姬云波, 童雄, 叶国华. 提钒技术的研究现状和发展[J]. 国外金属矿选矿, 2007, 5(8): 10-13.
[2] 王俊, 孙朝晖, 余晓春, 等. 高钙高磷钒渣提钒工艺研究进展[J]. 金属矿山, 2014, 456(6): 79-82.
[3] 付自碧. 钒钛磁铁矿提钒工艺发展历程及趋势[J]. 中国有色冶金, 2011, 12(6): 29-33.
[4] 孙朝晖. 钒新技术及钒产业发展前景分析[J]. 钢铁钒钛, 2012, 33(1): 1-7.
[5] 古映莹, 庄树新, 钟世安. 硅质岩钒矿中提取钒的无污染焙烧工艺研究[J]. 稀有金属, 2007, 31(1): 102-106.
[6] 朱保仓. 高碳石煤提钒新工艺研究[D]: [硕士学位论文]. 西安: 西安建筑科技大学, 2007.
[7] 史玲, 王娟, 谢建宏. 钠化法提钒工艺条件的研究[J]. 矿冶工程, 2008, 28(1): 58-61.
[8] 范鹤林, 陈登福, 徐松, 等. 高钙钒比钒渣钠化焙烧熟料浸出条件研究[J]. 过程工程学报, 2013, 13(6): 968-963.
[9] 张辉. 利用正交试验确定钒渣焙烧的最佳工艺条件[J]. 无机盐工业, 2003, 35(3): 29-31.
[10] 范鹤林, 陈登福, 徐松, 等. 高钙钒比钒渣钠化焙烧熟料浸出条件研究[J]. 过程工程学报, 2013, 13(6): 958-963.
[11] 李中军, 庞锡涛, 刘长让. 淅川钒矿钠化焙烧过程中热学性能、物相变化及钒氧化态变化的研究[J]. 化工冶金, 1993, 14(2): 123-129.