赤泥基铁水预处理脱硅脱磷剂的设计与开发
Design and Development of Red Mud-Based Desilication and Dephosphorization Agent for Hot Metal Pretreatment

DOI: 10.12677/MEng.2017.42020, PDF, HTML, XML, 下载: 898  浏览: 1,777 

作者: 宁国山, 孙嘉丽, 张 驰, 张 波, 刘承军, 姜茂发:东北大学冶金学院,辽宁 沈阳

关键词: 拜耳法赤泥改质熔化性能铁水预处理脱硅脱磷Bayer Red Mud Chemical Modification Melting Property Hot Metal Pretreatment Desilication and Dephosphorization

摘要: 本文对拜耳法赤泥进行改质后制备出一种铁水预处理脱硅脱磷剂,在其熔化性能测定的基础上,进行了铁水预处理脱硅脱磷高温模拟实验研究。研究结果表明:在赤泥中适量加入CaO进行改质,可显著降低赤泥的熔点,提高其熔化速度。利用赤泥与CaO质量比为100:30的赤泥基脱硅脱磷剂进行铁水预处理,铁水脱硅率达到98.2%,脱磷率达到75.5%,脱硅脱磷效果显著。
Abstract: A novel desilication and dephosphorization agent for hot metal pretreatment was designed and developed by the chemical modification of Bayer red mud. According to the determination results of melting properties for the red mud-based desilication and dephosphorization agent, the simulation experiment of the hot metal pretreatment was carried out at high temperature, and the results were shown as follows. The melting properties of the red mud-based desilication and dephosphorization agent could be improved remarkably by a proper addition of CaO. The red mud-based desilication and dephosphorization agent with the mass ratio of 100:30 for red mud and CaO was used in the simulation experiment process of the hot metal pretreatment. The desilication ratio and the dephosphorization ratio in the hot metal reached 98.2% and 75.5%, respectively.

文章引用: 宁国山, 孙嘉丽, 张驰, 张波, 刘承军, 姜茂发. 赤泥基铁水预处理脱硅脱磷剂的设计与开发[J]. 冶金工程, 2017, 4(2): 134-140. https://doi.org/10.12677/MEng.2017.42020

参考文献

[1] 张鹏科, 杨印东, 李光强. 用赤泥进行铁水预处理[J]. 矿业快报, 2005, 21(3): 26-30.
[2] 杨征, 石晓慧. 赤泥: 破解环保难题[J]. 中国有色金属, 2010(9): 54-55.
[3] 梁媛, 陈均宁. 赤泥的危害及综合利用[J]. 大众科技, 2014(7): 33-34.
[4] Kaida, Y., Hasegawa, M., Iwase, M., et al. (2005) A New Experimental Technique for Determinations of the Activities of P2O5 and FexO—The System CaO-P2O5-FexO. Metallurgical and Materials Transactions B, 36, 43-51.
https://doi.org/10.1007/s11663-005-0004-5
[5] Tamura, T., Nagasaka, T. and Hino, M. (2004) Phase Equilibria of Two-Liquid CaO-MgO-FetO-P2O5 Slag Saturated with (Mg, Fe)O. ISIJ Internatianal, 44, 476-481.
https://doi.org/10.2355/isijinternational.44.476
[6] 林成城, 施月循. 不同脱硅剂对铁水脱硅效果的研究[J]. 宝钢技术, 1999(6): 29-32.
[7] Yoshida, K., Yamazaki, I., Tozaki, Y., et al. (1990) Development of Effective Refining Process Consisting of Both Hot Metal Pretreatment and Decarburization in Two Top and Bottom Blown Converters. Tetsu-to-Hagane, 11, 1817-1822.
https://doi.org/10.2355/tetsutohagane1955.76.11_1817
[8] Ina, M. (1991) Metallurgical Characteristics of LD Type Hot Metal Pretreatment. Current Advances in Materials and Processes, 4, 1154.
[9] Wakamatsu, S.I. (1996) Dephosphorization at Hot Metal Pretreatment in a BOF Vessel. Current Advances in Materials and Processes, 9, 864.
[10] Kitamura, S.Y., Yonezawa, K., Ogawa, Y., et al. (2002) Improvement of Reaction Efficiency in Hot Metal Dephosphorization. Ironmaking and Steelmaking, 29, 121-124.