模压成型环氧树脂基复合材料的制备及性能研究
Preparation and Study of Properties of Epoxy Resin Matrix Composite by Molding
摘要: 以牌号为K20和HGS8000X的空心玻璃微珠为环氧树脂的填充材料，采用模压法制备了环氧树脂基复合材料，对其上、中、下三部分的密度、压缩强度及微观结构进行了测试和观察，比较了微珠的不同体积比对复合材料性能的影响。结果表明，不同粒径的空心玻璃微珠混合填充，有利于复合材料密度的降低，而且采用混合微珠制备的复合材料具有较好的性能均一性；微珠堆积系数越大，材料性能均一性越好。
Abstract: The epoxy resin matrix composite which was filled with hollow glass microspheres (HGMs) was prepared by molding. Two kinds of HGMs were K20 and HGS8000X. By testing and observing the density, compression strength and microstructure of different parts of the composite, the impact of volume fraction of HGMs on properties of the composite was compared. The results showed that: it was beneficial to get a lower density by mixing HGMs of different diameters; the homogeneity of the composite which was prepared by mixed HGMs was better; the higher accumulation coefficient of the HGMs was, the better homogeneity of the composite was.
文章引用：徐玉磊, 戴金辉, 吴平伟, 刘文栋, 刘青, 展飞. 模压成型环氧树脂基复合材料的制备及性能研究[J]. 材料科学, 2014, 4(2): 36-42. https://dx.doi.org/10.12677/MS.2014.42007

参考文献

[1] 周金磊, 戴金辉, 吴平伟等 (2013) 环氧树脂基固体浮力材料的制备及性能研究. 材料开发与应用, 2, 59-65.
[2] 朱志斌, 吴平伟 (2009) 深海探测用高强轻质浮力材料的研究与发展. 现代陶瓷技术, 1, 15-20.
[3] 乔英杰, 韩哲, 陈俊英等 (2012) 树脂基深水浮力材料压缩性能研究. 材料科学与工艺, 3, 46-50.
[4] 潘顺龙, 张敬杰, 宋广智 (2009) 深潜用空心玻璃微珠和固体浮力材料的研制及其研究现状. 热带海洋学报, 4, 17-21.
[5] Sanchez, S.M., Pages, P., Lacorte, T., et al. (2007) Curing FTIR study and mechanical characterization of glass bead filled tri-functional epoxy composites. Composites Science and Technology, 67, 1974-1985.
[6] 姜鑫, 李慧剑, 徐海涛等 (2012) HGB周期增强复合材料有效性能及界面应力场数值分析. 塑料工业, 1, 82-85.
[7] 卢子兴, 王嵩, 李忠明等 (2006) 空心微珠填充聚氨酯复合泡沫塑料的宏、细观力学性能. 航空学报, 5, 800-804.
[8] 李慧剑, 梁希等 (2011) 空心玻璃微珠填充环氧树脂复合材料力学性能试验研究. 燕山大学学报, 1, 46-51.
[9] 许磊, 宁荣昌, 朱艳 (2007) 空心玻璃微球填充环氧树脂模型材料的研制. 塑料工业, 7, 9-11.
[10] 何长军, 李慧剑等 (2009) 基于均匀设计的空心玻璃微珠改性环氧树脂配方研究. 中国塑料, 12, 48-51.
[11] 潘鹏举, 单国荣, 黄志明等 (2004) 空心玻璃微珠填充环氧树脂复合材料压缩性能研究. 中国塑料, 8, 78-92.
[12] 孙春宝, 邢奕, 王锋 (2006) 空心玻璃微珠填充聚合物合成深海高强浮力材料. 北京科技大学学报, 6, 554-558.

为你推荐