锂离子电池用LiMn0.58Fe0.42PO4前驱体Mn0.58Fe0.42CO3工艺研究
Process Study on the Mn0.58Fe0.42CO3 Precursor for Lithium-Ion Battery Cathode Material LiMn0.58Fe0.42PO4
摘要: 本文针对磷酸锰铁锂(LMFP)正极材料碳酸锰铁前驱体制备，采用液相共沉淀法，通过调控金属液浓度，成功制备出锰铁元素高度均匀分布的碳酸锰铁前驱体，并继承到了该前驱体所制备的LMFP正极材料中、该LMFP材料压实密度达到2.3517 g/cm3，0.1C克容量为155.25 mAh/g，1C克容量为146.19 mAh/g，1C循环200周容量保持率为95.1%。
Abstract: This paper focuses on the preparation of manganese iron carbonate precursor for lithium manganese iron phosphate (LMFP) cathode materials. Utilizing a liquid-phase co-precipitation method and regulating the concentration of the metal salt solution, a Mn0.58Fe0.42CO3 precursor with a highly uniform distribution of Mn and Fe elements was successfully synthesized. This elemental uniformity was effectively inherited by the resulting LiMn0.58Fe0.42PO4 cathode material. The as-prepared LMFP material exhibited a tap density of 2.3517 g/cm3, a specific discharge capacity of 155.25 mAh/g at 0.1C, and 146.19 mAh/g at 1C. Furthermore, it demonstrated excellent cycling stability, retaining 95.1% of its initial capacity after 200 cycles at a 1C rate.
文章引用：徐斌, 席多祥, 曹玉龙, 陈源, 杨长虹, 冯宛芡. 锂离子电池用LiMn0.58Fe0.42PO4前驱体Mn0.58Fe0.42CO3工艺研究[J]. 材料化学前沿, 2026, 14(3): 402-411. https://doi.org/10.12677/amc.2026.143037

参考文献

[1] Vanaphuti, P., Scanlan, K. and Manthiram, A. (2024) Ammonia-Free Synthesis of Lithium Manganese Iron Phosphate Cathodes via a Co-Precipitation Reaction. RSC Sustainability, 2, 1969-1978.
https://doi.org/10.1039/d4su00125g
[2] Minh, D.V., Ri, V., Lim, J., Nam, N.C., Hieu, N.M. and Kim, C. (2025) Synthesis of Highly Dense and Spherical Carbonate Mn0.5Fe0.5CO3 Precursor for LiMn0.5Fe0.5PO4 Cathode Material. Electronic Materials Letters, 21, 590-598.
https://doi.org/10.1007/s13391-025-00575-7
[3] Xiong, Y., Liu, D., Li, H., Tian, S., Liu, L., Liu, X., et al. (2026) Development and Industrialization Prospects of Lithium Manganese Iron Phosphate Cathode Material Technology. Journal of Energy Storage, 166, Article ID: 122440.
https://doi.org/10.1016/j.est.2026.122440
[4] Cao, Y.L., Chen, Z., Liu, P. and Xie, Y. (2026) N Doping Promotes the Multiplication Capability and Cycling Stability of Cobalt-Free Lithium-Rich Layered Cathode Materials. Journal of Power Sources, 661, Article ID: 238623.
https://doi.org/10.1016/j.jpowsour.2025.238623
[5] Olivetti, E.A., Ceder, G., Gaustad, G.G. and Fu, X. (2017) Lithium-Ion Battery Supply Chain Considerations: Analysis of Potential Bottlenecks in Critical Metals. Joule, 1, 229-243.
https://doi.org/10.1016/j.joule.2017.08.019
[6] 刘德波, 张萍, 杨丁诚, 等. 具有高导电性的镁掺杂LiMn0.6Fe0.4PO4/C复合物正极材料的性能研究 [J]. 黄河科技学院学报, 2025, 27(8): 9-17.
[7] Liu, P., Cao, Y., Chen, Z. and Xie, Y. (2025) Enhancement of Cathode Superior Kinetics and Li-Storage Properties of LiMn0.5Fe0.5PO4@c Cathode Materials by Ni Doping Strategy. Electrochimica Acta, 524, Article ID: 145991.
https://doi.org/10.1016/j.electacta.2025.145991
[8] 徐斌, 席多祥, 丁一娇, 冯宛芡, 杨萍. 液相共沉淀法制备磷酸锰铁前驱体工艺研究及应用[J]. 材料科学, 2026, 16(2): 193-204.
[9] Wang, M., Wu, H., Nan, H. and Luo, J. (2026) High Rate LiMn0.6Fe0.4PO4 Prepared by a Carbonate Precursor and Al2O3 Coating. Electrochimica Acta, Article ID: 149540.
https://doi.org/10.1016/j.electacta.2026.149540
[10] 袁明哲, 李天祥, 顾小玉, 等. 锂离子电池正极材料磷酸锰铁锂前驱体研究进展[J]. 生态产业科学与磷氟工程, 2026, 41(3): 62-70.
[11] 王智君, 宫东杰, 罗显明, 等. 一种复合多晶结构石墨烯磷酸锰铁锂及其制备方法和应用: CN115133025B [P]. 2025-09-19.
[12] 贾雨, 陈慧, 刘梦娜, 等. 共沉淀法可控制备磷酸锰铁锂正极材料研究进展[J]. 储能科学与技术, 2026, 15(2): 419-434.
[13] 童功松, 李智, 梁富忠. 两步法共沉淀制备磷酸锰铁[J]. 化工管理, 2025(21): 152-154.
[14] 唐杰峰, 王子俊, 陈奇志, 等. 磷酸锰铁锂正极材料的制备与改性策略[J]. 中国锰业, 2024, 42(4): 1-9+19.