改性纳米SiO2提高聚氨酯封堵性能研究
Study on Improving Plugging Performance of Polyurethane Plugging Agent by Modified Nano-SiO2
DOI: 10.12677/JAPC.2018.72009, PDF,   
作者: 卢小波：中国科学院理化技术研究所，北京;中国科学院大学，北京；路 遥*：中国科学院理化技术研究所，北京
关键词: 聚氨酯；堵剂；封堵；纳米SiO2；Polyurethane； Plugging Agent； Plugging； Nano-SiO2
摘要: 本文针对开采石油采出液含水高的问题，进行堵水技术研究。采用偶联剂KH-560对纳米SiO2进行改性，制备改性纳米SiO2/聚氨酯堵剂并进行封堵测试。结果表明，添加改性纳米SiO2后的堵剂，明显提高了耐温封堵性能。添加含量5%改性纳米SiO2的堵剂，使封堵温度达到100℃，封堵效率99%。并具有堵水不堵油的显著效果。
Abstract: In this paper, the water plugging technology is studied, in view of the problem of high water cut of oil recovery fluid. The nano-SiO2 was modified by silane coupling agent KH-560. The plugging test of the modified nano-SiO2/polyurethane composite plugging agent was carried out. After adding modified nano-SiO2, the results show that the plugging agent obviously improves the sealing performance of temperature resistance. Plugging temperature of 5% modified Nano-SiO2 plugging agent can reach 100˚C, the plugging efficiency is 99%, and the effect of water plugging and non-blocking oil is remarkable.
文章引用：卢小波, 路遥. 改性纳米SiO2提高聚氨酯封堵性能研究[J]. 物理化学进展, 2018, 7(2): 70-77. https://doi.org/10.12677/JAPC.2018.72009

参考文献

[1] 王玉普, 刘义坤, 邓庆军. 中国陆相砂岩油田特高含水期开发现状及对策[J]. 东北石油大学学报, 2014, 38(1): 1-9.
[2] 刘益军, 王毅, 赵晖, 卢安琪. 聚氨酯灌浆材料评述[J]. 粘接, 2005(4): 40-42.
[3] 李慧媛, 吴清林, 周定国. 纳米二氧化硅/纳米纤维素复合材料制备及性能分析[J]. 农业工程学报, 2015, 31(7): 299-303.
[4] 崔旭, 赵宝华, 张立博, 柳翱, 李东风. KH-560修饰纳米SiO2及其改性酚醛泡沫的制备和表征[J]. 化工新型材料, 2015, 43(11): 101-104.
[5] 陈姚, 赵苗苗, 于欣伟, 王步华, 张庆. KH570改性纳米SiO2的制备及应用[J]. 电镀与涂饰, 2014, 33(18): 783-787.
[6] 陈永军, 卿宁, 赵燕, 侯发秋, 何金文. 纳米二氧化硅改性水性聚氨酯分散液的制备与表征[J]. 涂料工业, 2014, 44(1): 40-45.
[7] 黄晓义, 路遥, 牟绍艳. 超声波催化亚硫酸氢钠封闭异氰酸酯[J]. 现代化工, 2011, 31(9): 50-51+53.
[8] 任龙芳, 张健, 强涛涛, 李梦函, 李霄. 聚酯二元醇的合成及水性聚氨酯的制备及其性能[J]. 陕西科技大学学报(自然科学版), 2017, 35(1): 28-34.