40吨钢包烘烤工艺的优化与分析
Optimization and Analysis of 40 t Steel Ladle Baking Process
摘要:
为节约能源降低成本，在差热分析的基础上提出了钢包烘烤新工艺，并开展现场实验和分析。采集新烘烤工艺下钢包包壳温度场数据，通过对终点温度分布和不同阶段升温速率的分析，发现采用新烘烤工艺的钢包达到了热饱和状态，能满足安全生产要求。
Abstract:
In order to save energy and reduce the cost, on the basis of analyzing the DTA-TGA date, a new process of steel ladle baking was put forward, and the field test was done. In the new baking process, temperature field data of the steel ladle shell were collected. Through analyzing the data of temperature distribution in the end point and heating rate in different stages, a conclusion was reached, and the steel ladle can reach the thermal saturation state and satisfy the requirement of safety in production in the new baking process.
参考文献
|
[1]
|
程本军, 等. 整体浇注钢包烘烤过程中内衬温度场和应力场分析[J]. 硅酸盐学报, 2012, 31(1): 25-26.
|
|
[2]
|
马鞍山钢铁股份有限公司长材事业部. 连铸工艺技术规程(2015版) [Z]. 17-19.
|
|
[3]
|
陈颖, 李春红, 等. 组合浇注整体包底减少钢包烘烤时间的探析[J]. 中国新技术新产品, 2013, 250(12): 125-126.
|
|
[4]
|
冯聚和, 等, 编. 铁水预处理与钢水炉外精炼[M]. 北京: 冶金工业出版社, 2006: 242-243.
|
|
[5]
|
刘占增, 郭鸿志. 钢包传热研究的发展现状[J]. 钢铁研究, 2007, 35(1): 59-61.
|
|
[6]
|
金从进, 丘文冬, 等. 烘烤过程钢包包壁温度场的有限元研究[J]. 耐火材料, 2001, 35(1): 24-35.
|
|
[7]
|
饶荣水. 钢包烘烤技术的发展[J]. 工业加热, 2000(3): 8-10.
|
|
[8]
|
李淑芬. 钢包烘烤装置的发展[J]. 冶金能源, 2003, 22(3): 37-39.
|
|
[9]
|
吴光亮, 朱荣, 等. 蓄热式钢包烘烤装置优化设计[J]. 特殊钢, 2003, 24(1): 24-26.
|
|
[10]
|
李丽丽, 郑丽君, 等. 富氧蓄热式钢包烘烤工艺技术可行性研究[J]. 材料与冶金学报, 2015, 14(3): 171-174.
|
|
[11]
|
周海球. 热分析技术在陶瓷材料烧结过程中的应用研究[D]: [硕士学位论文]. 长沙: 湖南大学, 2012: 7-9.
|
|
[12]
|
陆富汉, 唐捷. 钢包烘烤新工艺的开发和应用[C]//中国金属学会. 2004全国能源与热工学术年会论文集. 北京: 中国金属学会, 2004: 27-28.
|
|
[13]
|
潘树敏, 张征辉, 等. 邯宝炼钢厂250t 包烘烤研究[C]//中国金属学会. 第八届(2011)中国钢铁年会论文集. 北京: 中国金属学会, 2011.
|
|
[14]
|
田乃媛, 梁柏勇, 等. 迁钢210t钢包烘烤过程热测试[J]. 冶金能源, 2009, 28(6): 54-55.
|