负载型Mn基催化剂催化氧化甲苯的研究
Study on the Catalytic Oxidation of Toluene by Mn-Based Supported Catalysts
DOI: 10.12677/HJCET.2019.94043, PDF,    科研立项经费支持
作者: 杨仲余, 潘华*, 毛益萍, 王晟康, 张鼎盛, 王莉：浙江树人大学生物与环境工程学院，浙江 杭州
关键词: 甲苯；催化氧化；锰基催化剂；Toluene； Catalytic Oxidation； Mn-Based Supported Catalysts
摘要: 采用溶胶–凝胶法制备了CeO2和TiO2载体，通过浸渍法制备了Mn/CeO2和Mn/TiO2催化剂，通过催化活性评价和催化表征等方法考察了Mn/CeO2和Mn/TiO2等催化剂氧化甲苯的催化行为。研究表明：催化剂活性为Mn/CeO2 > Mn/TiO2 > TiO2 > CeO2。Mn/CeO2催化剂具有最低的起燃温度(T50 = 180℃)，其在215℃下甲苯的转化效率可稳定在80%。Mn/CeO2和Mn/TiO2等催化剂的活性与催化剂的物化结构、催化剂的活性组分有关。相较于Mn/TiO2，Mn/CeO2具有较大的孔体积和比表面积。Mn/CeO2和Mn/TiO2催化剂的活性组分皆主要为Mn3O4。相较于Mn/TiO2，Mn/CeO2催化剂表面具有较高含量的Mn2+和表面氧(Osurf)。
Abstract: CeO2 and TiO2 supports were synthetized by sol-gel method, Mn/CeO2 and Mn/TiO2 catalysts were prepared by impregnation method. The catalytic behaviors of Mn/CeO2 and Mn/TiO2 for oxidation of toluene were investigated by catalytic activity evaluation and catalyst characterization. The results show that the activities of catalysts decrease in order of Mn/CeO2 > Mn/TiO2 > TiO2 > CeO2. Mn/CeO2 catalyst has the lowest light-off temperature (T50 = 180˚C); the conversion of toluene can reach 80% at 215˚C. The activity of Mn/CeO2, Mn/CeO2 and other catalysts is related to the physical and chemical structure and the active component of the catalyst. Compared with Mn/TiO2, Mn/CeO2 has higher pore volume and specific surface area compared with Mn/CeO2. The active component of both Mn/CeO2 and Mn/TiO2 is Mn3O4. Compared with Mn/TiO2, Mn/CeO2 catalyst has a higher concentration of Mn2+ and Osurf.
文章引用：杨仲余, 潘华, 毛益萍, 王晟康, 张鼎盛, 王莉. 负载型Mn基催化剂催化氧化甲苯的研究[J]. 化学工程与技术, 2019, 9(4): 305-312. https://doi.org/10.12677/HJCET.2019.94043

参考文献

[1] Kalogridis, C., Gros, V., Sarda-Esteve, R., et al. (2014) Concentrations and Fluxes of Isoprene and Oxygenated VOCs at a French Mediterranean Oak Forest. Atmospheric Chemistry and Physics, 14, 10085-10102. [Google Scholar] [CrossRef] 
[2] Klimont, Z., Streets, D.G., Gupta, S., et al. (2002) Anthropogenic Emissions of Non-Methane Volatile Organic Compounds in China. Atmospheric Environment, 36, 1309-1322. [Google Scholar] [CrossRef] 
[3] 黎维彬, 龚浩. 催化燃烧去除VOCs污染物的最新进展[J]. 物理化学学报, 2010, 26(4): 885-894.
[4] Li, W.B., Chu, W.B., Zhuang, M. and Hua, J. (2004) Catalytic Oxida-tion of Toluene on Mn-Containing Mixed Oxides Prepared in Reverse Microemulsions. Catalysis Today, 93-95, 205-209. [Google Scholar] [CrossRef] 
[5] Bertinchamps, F., Grégoire, C. and Gaigneaux, E.M. (2006) Systematic Investigation of Supported Transition Metal Oxide-Based Formulations for the Catalytic Oxidative Elimination of (Chloro)-Aromatics: Part Ⅱ: Influence of the Nature and Addition Protocol of Secondary Phases to VOX/TiO2. Applied Catalysis B: Environmental, 66, 10-22. [Google Scholar] [CrossRef] 
[6] Choudhary, V.R., Uphade, B.S. and Pataskar, S.G. (2002) Low Temperature Complete Combustion of Dilute Methane over Mn-Doped ZrO2 Catalysts: Factors Influencing the Reactivity of Lattice Oxygen and Methane Combustion Activity of the Catalyst. Applied Catalysis A, 227, 29-41. [Google Scholar] [CrossRef] 
[7] 邢涛, 邵芸, 王家宏, 等. Cr/γ-Al2O3对乙酸乙酯的催化燃烧[J]. 环境化学, 2009, 28(6): 818-822.
[8] Pan, H., Jian, Y., Chen, C., et al. (2017) Sphere-Shaped Mn3O4 Cata-lyst with Remarkable Low-Temperature Activity for Methyl-Ethyl-Ketone Combustion. Environmental Science & Technology, 51, 6288-6297. [Google Scholar] [CrossRef] [PubMed]
[9] He, C., Yu, Y.K., Shi, J.W., et al. (2015) Mesostructured Cu-Mn-Ce-O Composites with Homogeneous Bulk Composition for Chlorobenzene Removal: Catalytic Performance and Micro Activation Course. Materials Chemistry and Phycics, 157, 87-100. [Google Scholar] [CrossRef] 
[10] He, C., Liu, X.H., Shi, J.W., et al. (2015) Anionic Starch-Induced Cu-Based Composite with Flake-Like Mesostructured for Gas-Phase Prop anal Efficient Removal. Journal of Colloid and Interface Science, 454, 221-222. [Google Scholar] [CrossRef] [PubMed]
[11] Liu, Y.X., Dai, H.X., Deng, J.G., et al. (2014) Mesoporous Co3O4-Supported Gold Nanocatalysts: Highly Active for the Oxidation of Carbon Monoxide, Benzene, Toluene, and O-Xylene. Journal of Catalysis, 309, 408-418. [Google Scholar] [CrossRef] 
[12] 刘洪喜, 蒋业华, 詹兆麟, 等. PIIID复合强化处理轴承钢表面TiN膜层的XPS表征[J]. 光谱学与光谱分析, 2009, 29(9): 2585-2589.