重构蓝宝石表面诱导La0.7Sr0.3MnO3纳米结构及其性质研究
Study on the Properties of La0.7Sr0.3MnO3 Nanostructures Induced by Reconstruction of Sapphire surface
摘要: 二维La0.7Sr0.3MnO3纳米薄膜在由m面蓝宝石表面重构的具有纳米凹槽的横向纳米复合材料下制备。通过XRD测试样品晶体结构，确定样品物质组成，用原子力显微镜(AFM)测试薄膜表面形貌。我们通过范德堡法测试了薄膜温度–电阻(R-T)曲线来表征其金属-绝缘体转变(MIT)特性，发现在重构蓝宝石基片的不同取向，即在沟道的不同方向上，其MIT表现出各向异性。从磁化强度随温度的变化，我们发现LSMO薄膜显示出顺磁–铁磁(PM-FM)相变，并且在沟道的不同方向上，其PM-FM也表现出各向异性。
Abstract: Two-dimensional La0.7Sr0.3MnO3 nanofilms were prepared on transverse nanocomposites with nanogrooves reconstructed from the surface of sapphire with m surface. The crystal structure and the composition of the samples were determined by X-Ray Diffraction (XRD), and the surface morphology of the films was tested by atomic force microscope (AFM). The Vanderbilt method was applied to measure the temperature-resistance (R-T) curve of the films in order to characterize its MIT properties. It is found that the MIT of reconstructed sapphire substrate shows anisotropy in different orientations of channels. From the variation of magnetization intensity with temperature, we found that LSMO film showed paramagnetic-ferromagnetic (PM-FM) phase transition, and its PM-FM also showed anisotropy in different directions of the channel.
文章引用：王明洁, 吉彦达, 杨浩. 重构蓝宝石表面诱导La0.7Sr0.3MnO3纳米结构及其性质研究[J]. 应用物理, 2020, 10(2): 131-138. https://doi.org/10.12677/APP.2020.102016

参考文献

[1] Huczko, A. (2000) Template-Based Synthesis of Nanomaterials. Applied Physics A (Materials Science Processing), 70, 365-376. [Google Scholar] [CrossRef] 
[2] Wang, Q.R. (2018) Modified Emission of Polymer Films by Ultrathin Ag Nanoparticle Films. Vacuum, 157, 111-114. [Google Scholar] [CrossRef] 
[3] Lv, Y., Ma, J., Mi, W., et al. (2012) Characterization of β-Ga2O3 Thin Films on Sapphire (0001) Using Metal-Organic Chemical Vapor Deposition Technique. Vacuum, 86, 1850-1854. [Google Scholar] [CrossRef] 
[4] Tsivion, D., Schvartzman, M., Popovitz-Biro, R., von Huth, P. and Joselevich, E. (2011) Guided Growth of Millimeter-Long Horizontal Nanowires with Controlled Orientations. Science, 333, 1003-1007. [Google Scholar] [CrossRef] [PubMed]
[5] Mullins, W.W. (1961) Theory of Linear Facet Growth during Thermal Etching. Philosophical Magazine, 6, 1313-1341. [Google Scholar] [CrossRef] 
[6] Wecker, J., Holzapfel, B., Schultz, L. and Samwer, K. (1993) Giant Negative Magnetoresistance in Perovskitelike La2/3Ba1/3MnOx Ferromagnetic Films. Physical Review Letters, 71, 2331-2333. [Google Scholar] [CrossRef] 
[7] Heffelfinger, J.R. and Carter, C.B. (1997) Mechanisms of Surface Faceting and Coarsening. Surface Science, 389, 188-200. [Google Scholar] [CrossRef] 
[8] Jin, S., Tiefel, T.H., Mccormack, M., et al. (1994) Thousandfold Change in Resistivity in Magnetoresistive La-Ca-Mn-O Films. Science, 264, 413-415. [Google Scholar] [CrossRef] [PubMed]
[9] Uehara, M., Mori, S., Chen, C.H. and Cheong, S.-W. (1999) Percolative Phase Separation Underliescolossal Magnetoresistance in Mixed-Valent Manganites. Nature, 399, 560-563. [Google Scholar] [CrossRef] 
[10] Elbio, D., Hotta, T. and Moreo, A. (2001) Colossal Magnetoresistant Materials: The Key Role of Phase Separation. Physics Reports, 344, 1-153.
[11] Wolf, S.A. (2001) Spintronics: A Spin-Based Electronics Vision for the Future. Science, 294, 1488-1495. [Google Scholar] [CrossRef] [PubMed]
[12] Oksenberg, E., Popovitz-Biro, R., Rechav, K. and Joselevich, E. (2015) Guided Growth of Horizontal ZnSe Nanowires and Their Integration into High-Performance Blue-UV Photodetectors. Advanced Materials, 27, 3999-4005. [Google Scholar] [CrossRef] [PubMed]
[13] Rothman, A., Forsht, T., Danieli, Y., et al. (2018) Guided Growth of Horizontal ZnS Nanowires on Flat and Faceted Sapphire Surfaces. The Journal of Physical Chemistry C, 122, 12413-12420. [Google Scholar] [CrossRef] 
[14] Heffelfinger, J.R., Bench, M.W. and Carter, C.B. (1995) On the Faceting of Ceramic Surfaces. Surface Science, 343, L1161-L1166. [Google Scholar] [CrossRef] 
[15] Weiss, J.D. (2013) A Comparison of Two van-der-Pauw Measurement Configurations of Resistivity. Materials Science in Semiconductor Processing, 16, 1637-1644. [Google Scholar] [CrossRef] 

为你推荐