球团的焙烧特性与还原行为的研究
Research on Roasting Characteristics and Reduction Behavior of Pellets
DOI: 10.12677/MEng.2020.72012, PDF,    科研立项经费支持
作者: 张 闯, 周晓雷*：昆明理工大学，冶金与能源工程学院，云南 昆明
关键词: 球团；焙烧；还原；Hematite Pellets； Roasting； Reduction
摘要: 球团矿是一种重要的人造块状原料，它把精矿粉、溶剂的混合物在造球机中滚动成球，然后干燥、焙烧、固结，成为具有良好冶金性质的含铁原料。本文主要介绍了球团的焙烧特性与还原行为的研究。
Abstract: Pellet is an important man-made lump raw material. It rolls a mixture of concentrate powder and solvent into balls in a pelletizer, and then it is dried, roasted, and consolidated, becomes a ferrous raw material with good metallurgical properties. This article mainly introduces the research on roasting characteristics and reduction behavior of pellets.
文章引用：张闯, 周晓雷. 球团的焙烧特性与还原行为的研究[J]. 冶金工程, 2020, 7(2): 77-82. https://doi.org/10.12677/MEng.2020.72012

参考文献

[1] Chang, M. and De Jonghe, L.C. (1984) Whisker Growth in Reduction of Oxides. Metallurgical Transaction B, 15, 685-693. [Google Scholar] [CrossRef] 
[2] Sharma, T., Gupta, R.C. and Praksh, B. (1993) Effect of Firing Condition and Ingredients on the Swelling Behaviour of Iron Ore Pellets. ISIJ International, 33, 446-453. [Google Scholar] [CrossRef] 
[3] El-Geassy, A.A., Nasr, M.I. and Hessieh, M.M. (1996) Effect of Reducing Gas on the Volume Change during Reduction of Iron Oxide Compacts. ISIJ International, 36, 640-649. [Google Scholar] [CrossRef] 
[4] Nasr, M.I., Omar, A.A., Hessien, M.M. and Ei-Geassy, A.A. (1996) Carbon Monoxide Reduction and Accompanying Swelling of Iron Oxide Compacts. ISIJ International, 36, 167-171. [Google Scholar] [CrossRef] 
[5] Sun, H.P. (2006) Reaction Rates and Swelling Phenomenon of Fe-C Droplets in FeO Bearing Slag. ISIJ International, 46, 1560-1569. [Google Scholar] [CrossRef] 
[6] Bahgat, M. and Abdel Halim, K.S. (2009) Metallic Iron Whisker Formation and Growth during Iron Oxide Reduction: K2O Effect. Ironmaking and Steelmaking, 36, 379-387. [Google Scholar] [CrossRef] 
[7] Abdel Halim, K.S. and Bahgat, M. (2009) Metallic Iron Whisker Formation and Growth during Iron Oxide Reduction: Basicity Effect. Ironmaking and Steelmaking, 36, 631-640. [Google Scholar] [CrossRef] 
[8] El-Geassy, A.-H.A. and Nasr, M.I. (2007) Reduction Kinetics and Catastrophic Swelling of MnO2-Doped Fe2O3 Compacts with Co at 1073-1373K. ISIJ International, 47, 377-385. [Google Scholar] [CrossRef] 
[9] 范晓慧, 谢路奔, 甘敏, 陈许玲, 袁礼顺. 高镁球团焙烧特性及其固结强化机理[J]. 中南大学学报(科学自然版), 2013, 44(2): 449-454.
[10] 殷兆迁, 李千文, 付自碧, 王俊, 高官金. 钒渣钠化球团化焙烧技术研究[J]. 钢铁钒钛, 2016, 37(1): 18-21 + 26.
[11] 陈许玲, 刘树, 甘敏, 范晓慧. 高钛球团焙烧行为及其强化技术[J]. 工程科学学报, 2016, 38(7): 920-929.
[12] 范军, 贾彦忠, 梁德兰. 赤铁矿球团焙烧过程研究[C]//冶金研究中心. 2005年“冶金工程科学论坛”论文集. 北京: 冶金工业出版社, 2005: 26-30.
[13] 黄柱成, 易凌云, 彭虎, 姜涛. 焙烧温度对氧化球团性质及其气基直接还原过程的影响[J]. 中南大学学报(自然科学报), 2012, 43(8): 6-12.
[14] 夏雷阁, 苏步新, 李新宇, 张建良, 赵志星, 青格勒. 焙烧温度与球团矿强度和还原性的关系[J]. 烧结球团, 2014, 39(1): 21-24 + 39.
[15] 姜涛, 何国强, 李晓芹, 唐兆坤, 李光辉. 焙烧气氛对内配碳赤铁矿球团焙烧行为的影响[J]. 中南大学学报(自然科学报), 2009, 40(4): 851-856.
[16] 范建军, 张文平, 刘慈光, 赵国栋, 席玉明. 磁铁矿粉粒度对球团矿预热焙烧性能的影响[J]. 钢铁, 2014, 49(11): 20.
[17] 王学峰. 首钢溶剂性球试验研究[J]. 烧结球团, 2014, 29(2): 5-11.
[18] 王莉. 碱度对球团矿冶金性能的影响[J]. 烧结球团, 1996, 21(2): 22-24.
[19] 宋招权. MgO对球团矿质量的影响[J]. 球团烧结, 1996, 21(2): 22-24.
[20] 周明顺, 刘万山, 翟立委. 复合溶剂性球团的开发研究[J]. 中国冶金, 2006, 13(6): 23-27.

为你推荐