耐黄变环氧树脂的制备与性能研究
Study on Preparation and Properties of Yellowing-Resistance Epoxy Resin
DOI: 10.12677/MS.2020.1011104, PDF,   
作者: 张贵恩, 范晋锋*, 李炳章, 李 静, 王执乾：中国电子科技集团公司第三十三研究所，山西 太原
关键词: 环氧树脂；硅烷；改性；耐黄变；韧性；Epoxy Resin； Silane； Modified； Yellowing-Resistance； Toughness
摘要: 采用异丙烯氧基三(三甲基硅烷基)硅烷对双酚A型环氧树脂进行改性，然后以异佛尔酮二胺为固化剂，制备了耐黄变环氧树脂，并对其各项性能进行研究。结果表明，通过异丙烯氧基三(三甲基硅烷基)硅烷对环氧树脂进行改性，能有效改善环氧树脂的耐黄变性能，提高其玻璃化转变温度和力学性能，而且不会使黏度升高。
Abstract: The bisphenol A epoxy resin was modified by isopropenyloxytris (trimethylsilyl) silane. Then isophorondiamine was used as the curing agent to prepare the yellowing-resistant epoxy resin, and the properties of modified epoxy resin were analyzed. The results showed that the isopro-penyloxytris (trimethylsilyl) silane modified epoxy resin effectively improved the yellowing re-sistance, glass transition temperature and mechanical properties of epoxy resin without increasing its viscosity.
文章引用：张贵恩, 范晋锋, 李炳章, 李静, 王执乾. 耐黄变环氧树脂的制备与性能研究[J]. 材料科学, 2020, 10(11): 865-870. https://doi.org/10.12677/MS.2020.1011104

参考文献

[1] 黄文迎, 袁有学. 国内外白光LED封装胶发展现状分析[J]. 新材料产业, 2014(12): 8-11.
[2] 牟秋红, 李金辉. 功率型LED封装材料的研究现状及发展方向[J]. 山东科学, 2011, 24(5): 30-34.
[3] 崔佳, 曲敏杰, 刘伟, 等. LED环氧树脂封装材料研究进展[J]. 塑料科技, 2008, 36(8): 90-92.
[4] 刘瑞霞, 杨欣, 张瑛, 等. LED封装用有机硅环氧树脂研究进展[J]. 粘接, 2014(7): 41-45.
[5] 苏倩倩, 刘伟区, 侯孟华. 有机硅改性提高环氧树脂韧性和耐热性的研究[J]. 有机硅氟资讯, 2008, 25(1): 31-34.
[6] 张顺, 谢建良, 邓龙江. 有机硅改性环氧树脂耐热胶粘剂的研制[J]. 材料导报, 2006, 20(F05): 54-56.
[7] 徐双双, 李杰, 郭安儒. 有机硅改性耐高温环氧树脂研究进展[J]. 中国胶粘剂, 2018, 27(11): 46-52.
[8] 李木, 吴力立, 张超灿, 等. 高性能有机硅改性环氧树脂的研究进展[J]. 塑料工业, 2018, 46(7): 15-20+44.
[9] 郑泽禹, 魏铭, 刘晓芳, 等. 无溶剂有机硅改性环氧涂料的制备及其性能研究[J]. 表面技术, 2018, 47(12): 8-13.
[10] 林新冠, 周冰, 王成骏. 有机硅改性环氧树脂性能研究[J]. 广州化工, 2019, 47(18): 46-48+85.

为你推荐