基于提高生物镁合金耐腐蚀性能的研究进展
Research on Improving Corrosion Resistance of Biological Magnesium Alloys
摘要: 生物镁合金具有优良的综合力学性能，生物可降解吸收性和良好的生物相容性，在骨修复、心血管支架等方面具有光明的应用前景。然而，目前，生物镁合金在生理体液中仍存在耐腐蚀性差，降解速度过快的不足。本文综述了国内外关于提高镁合金耐腐蚀性常见的改良方法与制备工艺以及具体研究进展情况，概括了各研究方向存在的问题，且展望了镁合金在生物医疗领域的发展方向。
Abstract: Biological magnesium alloys have bright application prospects in bone repair and cardiovascular scaffolds due to their excellent comprehensive mechanical properties, biodegradable absorbability and good biocompatibility. However, at present, biological magnesium alloys still have the shortcomings of poor corrosion resistance and too fast degradation rate in physiological body fluids. In this paper, the common methods and preparation processes for improving the corrosion resistance of magnesium alloys at home and abroad as well as the specific research progress were reviewed, the existing problems in each research direction were summarized, and the development direction of magnesium alloys in the biomedical field was further prospected.
文章引用：柏兴盛, 李岚清, 王统毅, 张涵羽, 马思楠, 刘东屹, 孙金娥. 基于提高生物镁合金耐腐蚀性能的研究进展[J]. 材料科学, 2022, 12(5): 437-442. https://doi.org/10.12677/MS.2022.125046

参考文献

[1] 孙雪, 奚廷斐. 第三代生物医学材料与再生医学国内外市场需求的变化与发展[J]. 中国临床康复, 2005(26): 105-110.
[2] 于杰, 朱明康, 闻明, 张俊敏. 新型医用钛合金材料的研究进展[J]. 昆明理工大学学报(自然科学版), 2017, 42(3): 16-22. [Google Scholar] [CrossRef] 
[3] 郭洁, 唐舟, 朱伟. 表面改性在医用镁及镁合金材料研究中的应用[J]. 生物骨科材料与临床研究, 2009, 6(4): 38-41.
[4] 张晓旭. 医用AZ91D镁合金表面改性研究[D]: [硕士学位论文]. 重庆: 西南大学, 2013.
[5] Lensing, R., Behrens, P., Müller, P.P., Lenarz, T. and Stieve, M. (2014) In Vivo Testing of a Bioabsorbable Magnesium Alloy Serving as Total Ossicular Replacement Prostheses. Journal of Biomaterials Applications, 28, 688-696. [Google Scholar] [CrossRef] [PubMed]
[6] Schaller, B., Saulacic, N., Beck, S., et al. (2016) In Vivo Degradation of a New Concept of Magnesium-Based Rivet Screws in the Minipig Mandibular Bone. Materials Science & Engineering C, 69, 247-254. [Google Scholar] [CrossRef] [PubMed]
[7] 王彬. 化学转化膜对AZ80镁合金可降解性的影响[D]: [硕士学位论文]. 太原: 中北大学, 2020.
[8] 齐琳. 镁合金的表面处理及耐腐蚀性能研究[J]. 上海化工, 2015, 40(9): 14-20.
[9] 李丽华. AZ91D镁合金钛锆转化膜成膜机制及耐蚀性能研究[D]: [硕士学位论文]. 沈阳: 沈阳理工大学, 2016.
[10] Rudd, A.L., Carmel B.B. and Florina, M. (2000) The Corrosion Protection Afforded by Rare Earth Conversion Coatings Applied to Magnesium. Corrosion Science, 42, 275-288. [Google Scholar] [CrossRef] 
[11] 王伟. 用于提升镁合金防腐蚀及抗细菌黏附性能的表面处理方法的研究[D]: [硕士学位论文]. 长春: 吉林大学, 2020.
[12] 刘晓寒, 冯静, 屈文娟. AZ91镁合金表面MgFe2O4薄膜的溶胶-凝胶法制备及其耐蚀性能[J]. 材料保护, 2012, 45(2): 58-60+86.
[13] 伊跃军. 医用镁合金表面羟基磷灰石涂层制备的研究[D]: [硕士学位论文]. 长沙: 中南大学, 2012.
[14] 张春艳, 高家诚, 曾荣昌, 杨惠, 吴霞. 电化学沉积法制备镁基Ca-P生物陶瓷涂层的研究[J]. 功能材料, 2010, 41(6): 952-956+960.
[15] 贾长建, 韩少兵, 赵兵, 许春香, 张金山. Zn对生物镁合金Mg-Zr-Mn合金力学性能以及腐蚀性能的影响[J]. 中国铸造装备与技术, 2017(3): 1-5.
[16] 赵兵, 韩少兵, 贾长健, 许春香, 张金山. Gd对心血管支架用Mg-Zn-Gd-Zr合金的腐蚀性能的影响[J]. 中国铸造装备与技术, 2017(4): 7-10.
[17] 李梦君, 万天, 谢旭东, 朱雨辰, 吴守钢, 张娇, 宋述鹏. 含微量Nd镁基生物材料的研究现状[J]. 科技创新导报, 2016, 13(25): 59-60. [Google Scholar] [CrossRef] 
[18] 周世杰, 黄楠, 龚旭, 景凤娟, 游天雪. Mg-Zn-Mn、Mg-Zn-Sr三元生物镁合金的制备与研究[J]. 轻金属, 2013(11): 49-52.
[19] 李慕勤, 张爱琴, 彭书浩, 王晶彦. 镁合金表面超声微弧氧化载氟生物涂层耐磨性和耐蚀性[J]. 表面技术, 2017, 46(3): 40-46.
[20] 李建兴, 张源, 李静媛. 微量CaO对Mg-2Zn-0.5Sr医用镁合金显微组织、力学性能及抗腐蚀性能的影响[J]. 稀有金属材料与工程, 2019, 48(2): 463-472.
[21] 张楚琦, 席中仙, 李艳梅, 李青. 一种新型复合膜层的制备及其性能研究[J]. 功能材料, 2015, 46(24): 24138-24141.
[22] Shen, S.B., Cai, S., Li, Y., Ling, R., Zhang, F.Y., Xu, G.H. and Wang, F.W. (2017) Microwave Aqueous Synthesis of Hydroxyapatite Bilayer Coating on Magnesium Alloy for Orthopedic Application. Chemical Engineering Journal, 309, 278-287. [Google Scholar] [CrossRef] 

为你推荐