磷石膏陶粒混凝土的制备与研究进展
Preparation and Research Progress of Phosphogypsum Ceramsite Concrete
DOI: 10.12677/HJCE.2022.1110117, PDF,    科研立项经费支持
作者: 许姜鹏, 谢一铭, 董洪承：扬州大学建筑科学与工程学院，江苏 扬州
关键词: 工业固废；磷石膏；陶粒；轻质混凝土；Industrial Solid Waste； Phosphogypsum； Ceramsite； Concrete
摘要: 磷石膏作为化工厂生产磷酸时的副产物，主要成分为二水硫酸钙，整体呈酸性，含有磷酸、氟等有害物质，且放射性超标，露天堆存会对环境造成污染。将磷石膏与多种物料进行复合可以制备新型材料，其在性能、实用性等方面都不逊色于原材料，此举可以有效提高磷石膏的利用量，缓解因磷石膏堆存所引起的较为严重的环境问题，为环境治理提供了新途径。本文通过结合国内外相关学者对磷石膏、陶粒在建筑领域与桥梁工程的研究利用现状，探讨磷石膏与陶粒对混凝土性能的影响因素，并综合评价磷石膏、陶粒在新型混凝土中所发挥的作用。
Abstract: Phosphogypsum as a by-product of phosphoric acid production in chemical plants, the main component is calcium sulfate dihydrate, which is acid and contains phosphoric acid, fluorine and other harmful substances; and when the radioactivity exceeds the standard, open storage will cause environmental pollution. By combining phosphogypsum with a variety of materials, new materials can be prepared, which is not inferior to raw materials in terms of performance and practicability, and can effectively improve the utilization of phosphogypsum, alleviate the more serious environmental problems caused by the accumulation of phosphogypsum, and provide a new way for environmental governance. Based on the research and utilization status of phosphogypsum and ceramsite in the field of construction and bridge engineering by relevant scholars at home and abroad, this paper discusses the influencing factors of phosphogypsum and ceramsite on the performance of concrete, and comprehensively evaluates the role played by phosphogypsum and ceramsite in new concrete.
文章引用：许姜鹏, 谢一铭, 董洪承. 磷石膏陶粒混凝土的制备与研究进展[J]. 土木工程, 2022, 11(10): 1061-1069. https://doi.org/10.12677/HJCE.2022.1110117

参考文献

[1] 张占彦. 磷石膏制备相变储能基体材料工艺研究[D]: [硕士学位论文]. 郑州: 郑州大学, 2019.
[2] 李光明, 李霞, 贾磊, 吴金玲. 国内外磷石膏处理和处置概况[J]. 无机盐工业, 2012, 44(10): 11-13.
[3] 朱俭凯, 陈鹏. 推进宜昌矿业绿色发展[J]. 学习月刊, 2020(11): 40-42.
[4] 袁伟. 利用磷石膏制备墙体材料可行性研究[D]: [硕士学位论文]. 绵阳: 西南科技大学, 2009.
[5] 丁萌, 李建锡, 李兵兵. 磷石膏中杂质及预处理对α半水石膏性能的影响[J]. 环境工程学报, 2014, 8(9): 4017-4021.
[6] Geraldo, R.H., Costa, A.R.D., Kanai, J., Silva, J.S., Souza, J.D., Andrade, H.M.C., Gonçalves, J.P., Fontanini, P.S.P. and Camarini, G. (2020) Calcination Parameters on Phosphogypsum Waste Recycling. Construction and Building Materials, 256, Article ID: 119406.
[Google Scholar] [CrossRef] 
[7] 李美. 磷石膏品质的影响因素及其建材资源化研究[D]: [博士学位论文]. 重庆: 重庆大学, 2012.
[8] 袁鹏, 谭建红, 官洪霞, 蒋达波, 南鹏林. 磷石膏中有害杂质对环境影响的监测与评价[J]. 广东化工, 2013, 40(22): 124-125+104.
[9] 杨晓梅, 赵清. 磷石膏化学成分的ICP-AES 分析方法[J]. 硫磷设计与粉体工程, 2008(6): 36-40.
[10] 蒋达波, 谭建红, 袁鹏, 官洪霞, 南鹏林. 磷石膏中有害成分的无害化处理方法综述[J]. 吉林化工学院院报, 2014, 31(1): 33-36.
[11] Ai, Y. and Xie, S.-K. (2020) Hydration Mechanism of Gypsum-Slag Gel Materials. Journal of Materials in Civil Engineering, 32, Article ID: 04019326.
[Google Scholar] [CrossRef] 
[12] Wang, Q., Zhuang, S. and Jia, R. (2018) An Investigation on the Anti-Water Properties of Phosphorus Building Gypsum (PBG)-Based Mortar. Journal of Thermal Analysis and Calorimetry, 136, 1575-1585.
[Google Scholar] [CrossRef] 
[13] Hua, S., Wang, K., Yao, X., et al. (2015) Effects of Fibers on Mechanical Properties and Freeze-Thraw Resistance of Phosphogypsum-Slag Based Cementitious Materials. Construction and Building Materials, 121, 290-299.
[Google Scholar] [CrossRef] 
[14] 谭明洋, 相利学, 李国龙. 磷石膏在道路工程应用的研究现状[J]. 广州化工, 2016, 44(8): 37-38.
[15] Zhou, J., Li, X.Q., Zhao, Y., Shu, Z., Wang, Y.X., Zhang, Y. and Shen, X. (2020) Preparation of Paper-Free and Fiber-Free Plasterboard with High Strength Using Phosphogypsum. Construction and Building Materials, 243, Article ID: 118091.
[Google Scholar] [CrossRef] 
[16] 熊春杨. 磷石膏微波法制备建筑石膏及其性能研究[D]: [硕士学位论文]. 绵阳: 西南科技大学, 2020.
[17] Sadiqul Islam, G.M., Habib Chowdhury, F., Tanveer Raihan, M., Kumar Sikder Amit, S. and Rafiqul Islam, M. (2017) Effect of Phosphogypsum on the Properties of Portland Cement. Procedia Engineering, 171, 744-751.
[Google Scholar] [CrossRef] 
[18] Liu, S.H., Ouyang, J.Y. and Ren, J. (2020) Mechanism of Calcination Modification of Phosphogypsum and Its Effect on the Hydration Properties of Phosphogypsum-Based Supersulfated Cement. Construction and Building Materials, 243, Article ID: 118226.
[Google Scholar] [CrossRef] 
[19] 赵青林, 吴科佩. 磷石膏废物资源优利用浅析[J]. 河南建材, 2001(4): 7-9.
[20] 刘林佩. 陶粒混凝土预制空心墙板制备及性能研究[D]: [硕士学位论文]. 重庆大学, 2021.
[21] 李翔, 王晓龙. 高铁站候车大厅保温层中陶粒混凝土的应用[J]. 建材发展导向, 2022, 20(16): 25-28.
[22] 赵勇, 吴智伟, 谢卓文, 王晓峰. 装配复合模壳体系混凝土剪力墙抗震性能试验研究[J]. 土木工程学报, 2020, 53(11): 36-45.
[23] 李书明, 郑新国, 刘竞, 谢永江, 胡家林, 张旭. 钢管自密实轻骨料混凝土变形性能试验研究[J]. 硅酸盐通报, 2021, 40(5): 1497-1502+1528.
[24] 付达新. 轻骨料混凝土的研究现状与展望[J]. 中国建材科技, 2009, 18(6): 47-51.
[25] 雍本. 特种混凝土设计与施工[M]. 北京: 中国建筑工业出版社, 1993: 8-11.
[26] 钱慧丽, 杨宗华, 梁会忠. 轻集料的发展状况综述[J]. 商品混凝土, 2007(1): 5-7+23+74.
[27] 曾峥. 改性陶粒混凝土力学性能及收缩性能的影响研究[D]: [硕士学位论文]. 长沙: 湖南大学, 2018.
[28] 肖汉光, 卢俊辉, 高斌. 宜昌高强陶粒的应用研究[C]//湖北省土木建筑学会学术论文集(2000-2001年卷). [出版者不详], 2002: 535-541.
[29] 霍俊芳. 轻骨料混凝土的研究现状与发展[J]. 建筑技术, 2009, 40(4): 363-365.
[30] 冯国峰. 陶粒混凝土复合保温砌块在节能建筑中的应用[J]. 墙材革新与建筑节能, 2009(5): 40-42+4-5.
[31] 徐峰, 汪少华. 陶粒混凝土在高效屋面保温工程中的应用[J]. 房材与应用, 2002, 30(4): 16-18.
[32] 俞静. 陶粒混凝土自保温结构体系相关技术研究[D]: [硕士学位论文]. 宁波: 宁波大学, 2012.
[33] Sandvik, M. and Hammer, T.A. (1995) The Development and Use of High Performance Lightweight Aggregate Concrete in Norway. International Symposium on Structural Lightweight Aggregate Concrete, Vol. 3, Sandefjord, 20-24 June 1995, 15-19.
[34] 李明利, 李芳. 陶粒混凝土发展现状及研究进展[J]. 混凝土世界, 2010(9): 16-18.
[35] 张畅. 磷石膏与菱镁矿尾矿粉对砂浆及混凝土收缩性能的影响[D]: [硕士学位论文]. 长春: 吉林建筑大学, 2020.
[36] 许晴莹. 磷石膏陶粒泡沫混凝土及砌块的制备与性能研究[D]: [硕士学位论文]. 扬州: 扬州大学, 2022.
[37] 马林转, 宁平, 杨月红, 陈玉保. 磷石膏预处理工艺综述[J]. 磷肥与复肥, 2007(3): 62-63.
[38] 杨林. 利用磷石膏制备建筑材料的研究[D]: [硕士学位论文]. 绵阳: 西南科技大学, 2013.
[39] 于万增, 潘俊廷, 朱会荣, 等. 原状磷石膏用作混凝土添加剂的性能研究[J]. 新型建筑材料, 2020, 47(4): 28-30+42.
[40] 田恬. 磷石膏泡沫混凝土的制备及性能研究[D]: [硕士学位论文]. 绵阳: 西南科技大学, 2016.
[41] 李金鹏. 大掺量磷石膏预制混凝土砌块及路面基层水稳材料的设计与研究[D]: [硕士学位论文]. 合肥: 安徽建筑大学, 2022.
[42] 王贻远. 磷石膏制备胶凝材料和混凝土的研究[D]: [硕士学位论文]. 北京: 北京化工大学, 2014.
[43] 李辛庚, 闫风洁, 岳雪涛, 王学刚. 陶粒混凝土的研究进展[J]. 硅酸盐通报, 2020, 39(11): 3407-3418+3452.
[44] 王帅. 陶粒混凝土的试验研究[D]: [硕士学位论文]. 天津: 天津大学, 2012.
[45] 赵明霞. 轻集料混凝土的研究和应用[J]. 散装水泥, 2011(2): 45-47.
[46] 田融昕. 陶粒混凝土超长内隔墙板力学性能研究[D]: [硕士学位论文]. 扬州: 扬州大学,2019.
[47] 桂习云. 不同掺合料对陶粒混凝土路用性能的影响研究[D]: [硕士学位论文]. 重庆: 重庆交通大学, 2020.

为你推荐