水胶比和矿物掺合料对玻璃纤维增强砂浆性能影响研究
Study on the Effect of Water Binder Ratio and Mineral Admixtures on the Properties of Glass Fiber Reinforced Mortar
摘要: 本文通过试验研究了水胶比、矿物掺合料以及胶凝材料用量对玻璃纤维增强砂浆性能的影响，包括抗压强度、抗折强度和微观结构。得到以下结论：A3的强度值最优，28天抗压强度和抗折强度分别为65.6 MPa和5.7 MPa，相比A1增幅达到378.83%和71.69%，SEM显示微观结构最为密实，玻璃纤维与胶凝体系粘结良好。最优胶凝材料比例为：水泥:矿粉:硅灰:粉煤灰 = 55:15:0:30，水胶比0.40，胶凝材料总量400 kg/m
3。
Abstract:
This article investigated the effects of water binder ratio, mineral admixtures, and cementitious material content on the properties of glass fiber-reinforced mortar through experiments, including compressive strength, flexural strength, and microstructure. The following conclusions are drawn: A3 has the optimal strength value, the densest structure, with good adhesion between glass fiber and the cementitious system. The 28-day compressive strength and flexural strength are 65.6 MPa and 5.7 MPa, respectively, with an increase of 378.83% and 71.69% compared to A1. The optimal cementitious material ratio is cement:mineral powder:silica fume:fly ash = 55:15:0:30, with a water binder ratio of 0.40 and a total cementitious material volume of 400 kg/m3.
参考文献
|
[1]
|
张王田, 张云升, 吴志涛, 等. 玻璃纤维增强水泥基材料组成优化设计与性能[J]. 材料导报, 2019, 33(14): 2331-2336.
|
|
[2]
|
徐力, 余飞, 朱祥, 等. 纤维在水泥混凝土中的应用[J]. 粉煤灰, 2013, 25(6): 40-43.
|
|
[3]
|
徐义华, 王恒. 纤维增强混凝土研究进展与应用[J]. 四川建材, 2022, 48(4): 17-18.
|
|
[4]
|
乐东钊, 姜久红, 文韬, 等. 玻璃纤维掺量对混凝土流动性及力学性能的影响[J]. 湖北工业大学学报, 2020, 35(2): 92-95.
|
|
[5]
|
王原原, 孙仁娟, 武新胜, 等. 玻璃纤维对混凝土收缩开裂性能的影响研究[J]. 建材世界, 2015, 36(4): 11-13+18.
|
|
[6]
|
徐蕾. 玻璃纤维对水泥混凝土塑性开裂性能的影响[J]. 新型建筑材料, 2013, 40(10): 29-31.
|
|
[7]
|
何健辉. 玻璃纤维水泥收缩与开裂性能研究[D]: [硕士学位论文]. 广州: 广州大学, 2019.
|
|
[8]
|
亓松彬. 耐碱玻璃纤维在水泥混凝土砂浆中的应用研究[J]. 混凝土世界, 2016(10): 80-85.
|
|
[9]
|
康学伟. 玻璃纤维混凝土在修复桥面裂缝中的应用[J]. 交通世界(下旬刊), 2017(9): 78-79.
|
|
[10]
|
黄竹也, 范景峰, 陆少连. 玻璃纤维增强混凝土(GFRC)在现浇空心楼盖中的应用[J]. 科技创新导报, 2008(29): 49-50.
|