摘要: 随着全球能源需求的迅猛增长，氢能作为一种清洁、高效的能源，其重要性日益凸显。电解水作为制备氢气的理想方法，其效率的提升关键在于优化两个核心反应：析氧反应(OER)和析氢反应(HER)。然而，OER由于其复杂的四电子转移过程和缓慢的动力学特性，成为了限制电解水技术效率提升的关键瓶颈。为了深入研究OER的反应机制，本文借助沸石咪唑酯骨架(ZIF)材料的独特优势，将钴卟啉负载在ZIF材料上，制备了一系列以ZIF材料为基底的OER催化剂。电化学测试表明，钴卟啉@Ni/Co-ZIF复合材料在碱性条件下具有较好的析氧性能，在10 mA cm−2电流密度下的过电位为345 mV，Tafel斜率为95 mV dec−1，且拥有良好的稳定性。
Abstract: With the rapid growth of global energy demand, hydrogen energy as a clean and efficient energy carrier, its importance has become increasingly prominent. Water splitting is an ideal method for hydrogen production, and the key to improve its efficiency is to optimize two core reactions: Oxygen evolution (OER) and hydrogen evolution (HER). However, due to its complex four-electron transfer process and slow kinetic characteristics, OER has become a key bottleneck limiting the efficiency of electrolytic water technology. In order to further study the reaction mechanism of OER, a series of OER catalysts based on zeolite imidazolate framework (ZIF) were prepared by loading cobalt porphyrin on ZIF material with the advantage of ZIF. Electrochemical tests show that cobalt porphyrin@Ni/Co-ZIF material has good oxygen evolution performance with overpotential of 345 mV at 10mA cm−2 current density and Tafel slope of 95 mV dec−1, and good stability under alkaline conditions.
文章引用：张腾坤, 李士祥, 王磊鑫, 崔会会, 王金. 沸石咪唑酯骨架材料负载钴卟啉析氧反应的研究[J]. 物理化学进展, 2024, 13(3): 447-454. https://doi.org/10.12677/japc.2024.133049

参考文献

[1] Peng, L. and Wei, Z. (2020) Catalyst Engineering for Electrochemical Energy Conversion from Water to Water: Water Electrolysis and the Hydrogen Fuel Cell. Engineering, 6, 653-679. [Google Scholar] [CrossRef] 
[2] Sun, L., Han, L., Huang, J., Luo, X. and Li, X. (2022) Single-Atom Catalysts for Photocatalytic Hydrogen Evolution: A Review. International Journal of Hydrogen Energy, 47, 17583-17599. [Google Scholar] [CrossRef] 
[3] Risch, M. (2023) Reporting Activities for the Oxygen Evolution Reaction. Communications Chemistry, 6, Article No. 221. [Google Scholar] [CrossRef] [PubMed]
[4] Ma, W., Zhang, X., Li, W., Jiao, M., Zhang, L., Ma, R., et al. (2023) Advanced Pt-Based Electrocatalysts for the Hydrogen Evolution Reaction in Alkaline Medium. Nanoscale, 15, 11759-11776. [Google Scholar] [CrossRef] [PubMed]
[5] Lee, S., Lee, Y., Lee, G. and Soon, A. (2022) Activated Chemical Bonds in Nanoporous and Amorphous Iridium Oxides Favor Low Overpotential for Oxygen Evolution Reaction. Nature Communications, 13, Article No. 3171. [Google Scholar] [CrossRef] [PubMed]
[6] Zhang, T., Zhao, Y., Liu, F., Zheng, M., Shi, K., Liu, J., et al. (2024) Novel Cobalt Nanorods@ Cobalt-Platinum Nanoparticles for Electrocatalytic Hydrogen Evolution Reactions and Oxygen Evolution Reactions Study. International Journal of Hydrogen Energy, 58, 646-656. [Google Scholar] [CrossRef] 
[7] Wang, J., Xuan, H., Meng, L., Liang, X., Li, Y., Yang, J., et al. (2023) N, S Co-Doped NiCo2O4@comoo4/NF Hierarchical Heterostructure as an Efficient Bifunctional Electrocatalyst for Overall Water Splitting. International Journal of Hydrogen Energy, 48, 8144-8155. [Google Scholar] [CrossRef] 
[8] Han, Z., Song, X., Chen, Z., Pan, Y., Lai, X., Wang, D., et al. (2024) Half Etching of ZIF-67 Towards Open Hollow Nanostructure with Boosted Absorption Ability for Toxic Smoke and Fume in Epoxy Composites. Sustainable Materials and Technologies, 41, e01024. [Google Scholar] [CrossRef] 
[9] Fan, H., Ma, F., Liu, Z., Wang, W., Liu, Z., Liang, X., et al. (2024) ZIF-Derived N-Doped Carbon Nanorods Supporting Bimetallic CoFe Single-Atoms/nanoclusters as Bifunctional Oxygen Electrocatalysts for Stable Zn-Air Batteries. Rare Metals. [Google Scholar] [CrossRef] 
[10] Zhang, H., Zhao, M. and Lin, Y.S. (2019) Stability of ZIF-8 in Water under Ambient Conditions. Microporous and Mesoporous Materials, 279, 201-210. [Google Scholar] [CrossRef] 
[11] Butt, F.S., Safdar, M., Lewis, A., Mazlan, N.A., Radacsi, N., Fan, X., et al. (2023) Superhydrophobic ZIF-67 with Exceptional Hydrostability. Materials Today Advances, 20, Article 100448. [Google Scholar] [CrossRef] 
[12] Singh, R. and Mukherjee, A. (2019) Metalloporphyrin Catalyzed C-H Amination. ACS Catalysis, 9, 3604-3617. [Google Scholar] [CrossRef] 
[13] Wang, M., Zhang, M., Song, W., Zhou, L., Wang, X. and Tang, Y. (2022) Heteroatom-Doped Amorphous Cobalt-Molybdenum Oxides as a Promising Catalyst for Robust Hydrogen Evolution. Inorganic Chemistry, 61, 5033-5039. [Google Scholar] [CrossRef] [PubMed]
[14] Liang, Z., Guo, H., Zhou, G., Guo, K., Wang, B., Lei, H., et al. (2021) Metal-Organic-Framework-Supported Molecular Electrocatalysis for the Oxygen Reduction Reaction. Angewandte Chemie International Edition, 60, 8472-8476. [Google Scholar] [CrossRef] [PubMed]
[15] Andres-Garcia, E., Oar-Arteta, L., Gascon, J. and Kapteijn, F. (2019) ZIF-67 as Silver-Bullet in Adsorptive Propane/Propylene Separation. Chemical Engineering Journal, 360, 10-14. [Google Scholar] [CrossRef] 
[16] Trotochaud, L., Young, S.L., Ranney, J.K. and Boettcher, S.W. (2014) Nickel-Iron Oxyhydroxide Oxygen-Evolution Electrocatalysts: The Role of Intentional and Incidental Iron Incorporation. Journal of the American Chemical Society, 136, 6744-6753. [Google Scholar] [CrossRef] [PubMed]
[17] Anantharaj, S. and Noda, S. (2022) How Properly Are We Interpreting the Tafel Lines in Energy Conversion Electrocatalysis? Materials Today Energy, 29, Article 101123. [Google Scholar] [CrossRef] 
[18] Lin, D. and Lasia, A. (2017) Electrochemical Impedance Study of the Kinetics of Hydrogen Evolution at a Rough Palladium Electrode in Acidic Solution. Journal of Electroanalytical Chemistry, 785, 190-195. [Google Scholar] [CrossRef] 
[19] Li, F., Wang, P., Huang, X., Young, D.J., Wang, H., Braunstein, P., et al. (2019) Large-Scale, Bottom-Up Synthesis of Binary Metal-Organic Framework Nanosheets for Efficient Water Oxidation. Angewandte Chemie International Edition, 58, 7051-7056. [Google Scholar] [CrossRef] [PubMed]
[20] Jia, L., Liu, B., Zhao, Y., Chen, W., Mou, D., Fu, J., et al. (2020) Structure Design of MoS2@Mo2C on Nitrogen-Doped Carbon for Enhanced Alkaline Hydrogen Evolution Reaction. Journal of Materials Science, 55, 16197-16210. [Google Scholar] [CrossRef]