水射流辅助激光加热处理氮化硼表面硬化研究
Study on Surface Hardening of Boron Nitride in Composite Laser Water Injection Heat Treatment
摘要: 采用复合式CO2激光表面持续加热和水射流淬火相结合的新型热处理工艺对双相纤锌矿/立方氮化硼(wBN/cBN)表面进行改性处理，研究了水射流辅助激光热处理工艺对wBN/cBN硬度的影响。结果表明，伴随着快速淬火热处理的应力诱导相变和纳米尺寸晶粒的形成，双相wBN/cBN的维氏硬度最高可达到70 GPa，接近聚晶金刚石(PCD)的硬度。
Abstract: The surface of duplex wurtzite/cubic boron nitride (wBN/cBN) was modified by a new heat treat-ment process combining CO2 laser surface continuous heating and water jet quenching, the influ-ence of water jet assisted laser heat treatment on the hardness of wBN/cBN was studied. The re-sults show: With the stress-induced phase transition of the rapid quenching heat treatment and the formation of nano-sized grains, the vickers hardness of the two-phase wBN/cBN can reach 70 GPa, reaching the hardness of polycrystalline diamond (PCD).
文章引用：王树才. 水射流辅助激光加热处理氮化硼表面硬化研究[J]. 材料科学, 2021, 11(1): 25-30. https://doi.org/10.12677/MS.2021.111004

参考文献

[1] 王艳芝, 张旺玺, 孙长红, 等. 氮化硼系列材料的合成制备及应用研究进展[J]. 陶瓷学报, 2018, 39(6): 661-671.
[2] 贾凤. 高温高压下cBN单晶相变机理的理论计算研究[D]: [硕士学位论文]. 济南: 山东建筑大学, 2019.
[3] Melaibari, A.A., Wu, Z., Shrotriya, P., et al. (2016) Ultrahard Boron Nitride Material through a Hybrid Laser/Waterjet Based Surface Treatment. Acta Materialia, 102, 315-322. [Google Scholar] [CrossRef] 
[4] 张晨旭. 激光辅助水射流切割氧化铝陶瓷的可加工性研究[D]: [硕士学位论文]. 济南: 山东大学, 2016.
[5] 王良. 激光辅助水射流微细加工氮化硅陶瓷的去除机理与工艺研究[D]: [硕士学位论文]. 济南: 山东大学, 2017.
[6] 李启泉, 孙长红, 刘书锋. PcBN复合材料及其用作刀具的发展现状研究[J]. 中原工学院学报, 2019, 30(5): 1-7.
[7] 刘明耀, 李克华, 赵兴昊. 中国CBN磨具的研发历程与技术发展趋势[J]. 金刚石与磨料磨具工程, 2017, 37(1): 1-6.
[8] 陈超, 莫培程, 林峰, 等. cBN-TiN-Al合成PCBN复合片及其性能研究[J]. 中国陶瓷, 2019, 55(7): 36-41.
[9] Zhao, J., Wong, K.S. and Shrotriya, P. (2017) Hybrid CO2 Laser Waterjet Heat (LWH) Treatment of Bindered Boron Nitride Composites with Hardness Improvement. Ceramics International, 43, 8031-8039. [Google Scholar] [CrossRef] 
[10] 袁珠珠. 超声振动与射流辅助激光复合加工系统设计[D]: [硕士学位论文]. 合肥: 安徽建筑大学, 2018.
[11] 陈雪辉, 李翔, 吴超, 等. 水射流辅助激光加工碳化硅的影响研究[J]. 激光与光电子学进展, 2019, 56(1): 225-231.
[12] Ma, L., Wang, L., Li, C., et al. (2019) Hybrid Nanosec-ond Laser Processing and Heat Treatment for Rapid Preparation of Super-Hydrophobic Copper Surface. Metals, 9, 668. [Google Scholar] [CrossRef] 
[13] 于天彪, 贾闯, 于奎东, 等. 激光近净成形CBN磨具温度场仿真分析[J]. 激光与红外, 2019, 49(5): 523-528.
[14] 李良, 陈玉奇, 周爱国. 聚晶立方氮化硼用结合剂及其制备工艺的研究进展[J]. 金刚石与磨料磨具工程, 2019, 39(2): 46-50.
[15] Zhao, J., Guo, J., Shrotriya, P., et al. (2019) A Rapid One-Step Nanosecond Laser Process for Fabrication of Superhydrophilic Aluminum Surface. Optics & Laser Technology, 117, 134-141. [Google Scholar] [CrossRef] 
[16] 王永凯, 张相法, 位星, 等. 不同品种立方氮化硼热稳定性能的研究[J]. 金刚石与磨料磨具工程, 2017, 37(5): 66-68.
[17] 姚燕生, 陈庆波, 汪俊, 等. 氮化硅陶瓷水射流辅助激光精密加工[J]. 光学精密工程, 2018, 26(11): 2723-2731.
[18] 杨娜, 王农跃, 姚艳梅, 等. 氮化硼和纳米金刚石混杂填充聚酰亚胺导热复合材料的制备与表征[J]. 高分子材料科学与工程, 2017, 33(1): 153-157.
[19] 章辰. 水射流辅助激光切割碳纤维复合材料的研究[D]: [硕士学位论文]. 无锡: 江南大学, 2018.

为你推荐